300 Stainless grade

304 BA304 NO.4 ,304L NO.4

304 2B, 304L 2B , 316L 2B,316 2B

304Hard situation1/2H3/4HH
304 HL, 304L HL

400 Stainless grade

430 BA430 1D 430 NO.4

430 2DHard):1/2H250°-280°),3/4H290°-330°),H400°-450°

Stainless Width1000mm—1500mm

Stainless Thickness0.3mm—3.0mm

 

Mechanical properties of austenitic stainless steel

Stainless production specification

Grade Surface Thickness Width
201 2D 0.1-0.5mm 10-640mm
301 2D/DF(1/2H、3/4H、H、EH、SEH) 0.05-1.0mm 10-1240mm
304 BA/2BB HL 0.1-1.0mm 10-1240mm
2D/DF(1/2H、3/4H、H) 0.05-1.0mm 10-1240mm
316L/321 2BB 0.05-1.0mm 10-1240mm
316L/321 2D/DF(1/2H、3/4H、H) 0.05-1.0mm 10-1240mm
430 BA/2BB 0.1-1.5mm 10-1240mm
BA1 0.2-0.5mm 10-720mm
1D/2BD 0.1-1.5mm 10-1240mm
409/410S 1D/BA 0.1-1.5mm 10-1240mm
444 2D/DF(1/2H、H) 0.05-1.0mm 10-1240mm

 

Stainless steel sheets / coil /colour sheet .
Material: SS304, 201, 316, 316L,430,410,429

Raw surface : 2B/BA/NO.4/HL

Size (mm): 1000*2000, 1219*2438, 1219* 3048, or customize size

Thickness: 0.3-3 mm, 0.15-10mm sheet plate etc.

Surface: Mirror Surface, Hairline Surface, Sand Blast Surface, Vibration Surface, Etched Surface, Embossed Surface, 3D Surface

Parts of stainless grade property from our factory

SUS304 Stainless material

Surface Tensile Mpa Yield Mpa Elongation% Elongation%

Actual

Hardness(Hv) Actual factory hardness Hv(range 20)
2B ≥40 50–60 150-180 160-180
1/4H ≥620 ≥400 ≥15 35–50 210-240 215-235
1/2H ≥780 ≥470 ≥6 25–40 250-280 255-275
3/4H ≥930 ≥665 ≥3 20–30 310-340 315-335
H ≥1130 ≥880 ≥1 2–10 370-400 375-395

 SUS301 Stainless material

Surface Tensile Mpa Yield Mpa Elongation% Elongation%

Actual

Hardness(Hv) Actual factory hardness Hv(range 20)
soft ≥580 ≥205 ≥40 40–55 190-220 195-215
1/4H ≥770 ≥450 ≥20 25–40 250-280 260-280
1/2H ≥930 ≥510 ≥10 15–30 310-340 320-340
3/4H ≥1130 ≥754 ≥5 10–20 370-400 380-400
H ≥1320 ≥1030 5–15 430-460 430-450
EH1 ≥1570 ≥1275 0–1 490-520 500-520
EH2 ≥1740 ≥1450 0–1 530-560 540-560
SEH ≥2000 ≥1850 0–1 ≥580 ≥590

 

SUS201LH Stainless material

Surface Tensile Mpa Yield Mpa Elongation% Elongation%

Actual

Hardness(Hv) Actual factory hardness Hv(range 20)
soft ≥600 ≥400 35–40 35–40 210-250 According to po
1/2H ≥850 ≥470 15–35 15–35 250-280 According to po
3/4H ≥950 ≥600 20–30 20–30 310-340 According to po
H ≥1080 ≥750 5–20 5–20 370-400 According to po

 

SUS316Lstainless material

Surface Tensile Mpa Yield Mpa Elongation% Elongation%

Actual

Hardness(Hv) Actual factory hardness Hv(range 20)
软态 ≥40 50–60 140-170 145-165
1/4H ≥550 ≥330 ≥15 30–50 210-240 215-235
1/2H ≥730 ≥430 ≥6 20–40 250-280 255-275
3/4H ≥880 ≥620 ≥3 10–20 310-340 315-335
H ≥1050 ≥840 ≥1 2–10 360-390 365-385

For the above mechanical property parameters, 301 and 304 hard materials are in accordance with JISG4313-2011 standard, and soft materials are in accordance with JIS4305-2012 standard.